Material Constants Youngs' Modulus 'E' - Shear Modulus'G' - Poisson's Ratios 'v'

Material	E		G		Poisson's ratio n
	ksi	GPa	ksi	Gpa
Aluminum alloys	-	-	-	-	-
2014-T4	10,600	73	4,000	27.6	0.33
2014-T6	10,600	73	3,800	26.2	0.33
2024-T4	10,600	73	3,900	27	0.33
6061-T6	10,400	72	3,900	27	0.33
7075-T6	10,000	69	3,750	26	0.33
Brass (Red, cold rolled)	15,000	104	5,500	38	0.34
Brass (Red, annealed)	15,000	104	5,500	38	0.34
Bronze (cold rolled)	15,000	104	6,500	44.9	0.34
Bronze (annealed)	15,000	104	6,500	44.9	0.34
Cast iron (tension)	25,000	173	12,500	86.3	0.28
Cast iron (compression)	25,000	173	12,500	86.3	0.28
Concrete (compression)	4,500	31	-	-	0.15
Copper (cold-drawn)	17,000	117	6,300	43.5	.35
Plate glass	10,000	69	4,000	27.6	0.2
Magnesium alloy	24,000	166	20,000	138	0.35
Monel (wrough, hot rolled)	26,000	179	9,500	65.6	.32
Nickel alloy	30,000	207	11,400	78.7	0.31
Plastics	-	-	-	-	-
Nylon	400	2.76	-	-	0.4
Polyethylene	150	1	-	-	0.4
Rubber (average)	.4	.00276	.0007	41.5	0.48
Steel	-	-	-	-	-
.2% C hardened	30,000	207	11,600	80	.32
.2% C cold-rolled	30,000	207	11,600	80	.32
.2% C hot-rolled	30,000	207	11,600	80	.32
.4% C hot-rolled	30,000	207	11,600	80	.32
.8% C hot-rolled	30,000	207	11,600	80	.32
Stainless (cold-rolled)	29,000	200	12,500	86.3	.27
Stainless (heat-treated)	29,000	200	12,500	86.3	.27
Steel, structural	-	-	-	-	-
ASTM-A36	29,000	200	11,000	75.9	.32
ASTM-A572	29,000	200	11,000	75.9	.32
ASTM-A514	29,000	200	11,000	75.9	.32
Wood (comp.along grain)	-	-	-	-	-
Douglas Fir	1,300	9	-	-	.29
Southern Pine	1,900	13.1	-	-	.3
Red Oak	1,800	12.4	-	-	.3